Specifications of Glazed Frits
JT-1802
SINGLE FAST FIRING WALL TILE TRANSPARENT( CRYSTAL)FRIT
INGREDIENT: SiO 2 -Al 2 O 3 -B 2 O 3 -Na 2 O-ZnO-K 2 O-BaO-CaO-MgO
EXPANSIVE COEFFICIENT: 185(X10 -7 / ℃ )
INTENERATE TEMPERATURE: 770 ℃
CHARACTERISTICS: FINE SMOOTHNESS AND BRIGHT, TRANSPARENT AND COMFORTABLE COLOR, WITH A BROAD RANGE OF FIRING.
CONDITION FOR USE: SUITABLE FOR SINGLE FAST FIRING WALL TILE.
FIRING ENVIRONMENTAL TEMPERATURE: 1000℃--1040℃(27# TEMPERATURE RING), 1120℃--1150℃ GAUGE READINGS
RECOMMENDED RATIO: GENERAL
MATERIALS
USED |
RATIO RANGE
(GENERAL) |
RATIO
(SPECIFIC) |
JT-1802 |
90-92% |
92% |
KAOLIN |
8-12% |
8% |
CMC |
0.12-0.15% |
0.12% |
STPP |
0.22-O.30% |
0.30% |
H 2 O |
30-35% |
33% |
RECOMMENDED RATIO: ROTOCOLOR LARGE-SIZE
MATERIALS
USED |
RATIO RANGE
(GENERAL) |
RATIO
(SPECIFIC) |
JT-1802 |
60-90% |
66% |
JZ-1618 |
10-40% |
34% |
KAOLIN |
8-12% |
8% |
CMC |
0.12-0.15% |
0.10% |
STPP |
0.22-O.30% |
0.30% |
H 2 O |
30-35% |
33% |
PROCESS REQUIREMENT: GLAZE SLIP, SCREENED THROUGH 120MESH, IS APPLIED BY WAY OF A SCRAPER OR A BELL.
REMAINS: 4-6g/100cc(325MESH)
DENSITY: 1.82-1.84
FLOW:50-60SECONDS
JT-1819
SINGLE FAST FIRING WALL TILE TRANSPARENT( CRYSTAL)FRIT
INGREDIENT: SiO 2 -Al 2 O 3 -CaO-MgO-ZnO -B 2 O 3 -K 2 O -Na 2 O
EXPANSIVE COEFFICIENT: 200(X10 -7 / ℃ )
INTENERATE TEMPERATURE: 790 ℃
CHARACTERISTICS: FINE SMOOTHNESS AND BRIGHT, TRANSPARENT AND COMFORTABLE WHITENESS, FINE-COLOR AND WITH A BROAD RANGE OF FIRING.
CONDITION FOR USE: SUITABLE FOR SINGLE FAST FIRING WALL TILE.
FIRING ENVIRONMENTAL TEMPERATURE: 1000℃--1040℃(27# TEMPERATURE RING), 1120℃--1150℃ GAUGE READINGS
RECOMMENDED RATIO: GENERAL
MATERIALS
USED |
RATIO RANGE
(GENERAL) |
RATIO
(SPECIFIC) |
JT-1819 |
90-92% |
92% |
KAOLIN |
8-12% |
8% |
CMC |
0.12-0.15% |
0.12% |
STPP |
0.22-O.30% |
0.30% |
H 2 O |
30-35% |
33% |
RECOMMENDED RATIO: ROTOCOLOR LARGE-SIZE
MATERIALS
USED |
RATIO RANGE
(GENERAL) |
RATIO
(SPECIFIC) |
JT-1819 |
60-90% |
66% |
JZ-1618 |
10-40% |
34% |
KAOLIN |
8-12% |
8% |
CMC |
0.12-0.15% |
0.10% |
STPP |
0.22-O.30% |
0.30% |
H 2 O |
30-35% |
33% |
PROCESS REQUIREMENT: GLAZE SLIP, SCREENED THROUGH 120MESH, IS APPLIED BY WAY OF A SCRAPER OR A BELL.
REMAINS: 4-6g/100cc(325MESH)
DENSITY: 1.82-1.84
FLOW: 50-60SECONDS
JT-701
DOUBLE FAST FIRING WALL TILE TRANSPARENT( CRYSTAL)FRIT
INGREDIENT: SiO 2 -Al 2 O 3 -K 2 O-Na 2 O - CaO-MgO-B 2 O 3 -ZnO-BaO
EXPANSIVE COEFFICIENT: 185(X10 -7 / ℃ )
INTENERATE TEMPERATURE: 760 ℃
CHARACTERISTICS: FINE SMOOTHNESS AND BRIGHT, TRANSPARENT AND COMFORTABLE WHITENESS, WITH A.BROAD RANGE OF FIRING.
CONDITION FOR USE: SUITABLE FOR DOUBLE FAST FIRING WALL TILE.
FIRING ENVIRONMENTAL TEMPERATURE: 1000℃--1020℃(27# TEMPERATURE RING), 1060℃--1090℃ GAUGE READINGS.
RECOMMENDED RATIO: GENERAL
MATERIALS
USED |
RATIO RANGE
(GENERAL) |
RATIO
(SPECIFIC) |
JT-701 |
92-95% |
95% |
KAOLIN |
5-8% |
5% |
CMC |
0.12-0.15% |
0.12% |
STPP |
0.22-O.30% |
0.30% |
H 2 O |
33% |
33% |
PROCESS REQUIREMENT: GLAZE SLIP, SCREENED THROUGH 120MESH, IS APPLIED BY WAY OF A SCRAPER OR A BELL.
REMAINS: 4-6g/100cc(325MESH)
DENSITY: 1.82-1.84
FLOW: 50-60SECONDS
JT-1808
SINGLE FAST FIRING FLOOR TILE TRANSPARENT( CRYSTAL)FRIT
INGREDIENT: SiO 2 -Al 2 O 3 -Na 2 O-K 2 O-BaO-CaO-MgO-ZnO
EXPANSIVE COEFFICIENT: 200(X10 -7 / ℃ )
INTENERATE TEMPERATURE: 800 ℃
CHARACTERISTICS: FINE SMOOTHNESS AND BRIGHT, TRANSPARENT AND COMFORTABLE WHITENESS, WITH A BROAD RANGE OF FIRING.
CONDITION FOR USE: SUITABLE FOR SINGLE FAST FIRING WALL TILE.
FIRING ENVIRONMENTAL TEMPERATURE: 1040℃--1070℃(27# TEMPERATURE RING), 1150℃--1190℃ GAUGE READINGS
RECOMMENDED RATIO: GENERAL
MATERIALS
USED |
RATIO RANGE
(GENERAL) |
RATIO
(SPECIFIC) |
JT-1808 |
85-90% |
88% |
KAOLIN |
12-15% |
12% |
CMC |
0.12-0.15% |
0.12% |
STPP |
0.22-O.30% |
0.30% |
H 2 O |
33% |
33% |
PROCESS REQUIREMENT: GLAZE SLIP, SCREENED THROUGH 120MESH, IS APPLIED BY WAY OF A SCRAPER OR A BELL.
REMAINS: 5-7g/100cc(325MESH)
DENSITY: 1.82-1.84
FLOW: 50-60SECONDS
JT-90
DOUBLE FAST FIRING FLOOR TILE TRANSPARENT( CRYSTAL)FRIT
INGREDIENT: SiO 2 -Al 2 O 3 -K 2 O-Na 2 O-ZnO-B 2 O 3 -PbO-MgO-BaO
EXPANSIVE COEFFICIENT: 195(X10 -7 / ℃ )
INTENERATE TEMPERATURE: 770 ℃
CHARACTERISTICS: FINE SMOOTHNESS AND BRIGHT, TRANSPARENT AND COMFORTABLE WHITENESS, WITH A.BROAD RANGE OF FIRING.
CONDITION FOR USE: SUITABLE FOR DOUBLE FAST FIRING WALL TILE.
FIRING ENVIRONMENTAL TEMPERATURE: 1030℃--1050℃(27# TEMPERATURE RING), 1120℃--1150℃ GAUGE READINGS.
RECOMMENDED RATIO: GENERAL
MATERIALS
USED |
RATIO RANGE
(GENERAL) |
RATIO
(SPECIFIC) |
JT-90 |
90-92% |
92% |
KAOLIN |
8-10% |
8% |
CMC |
0.12-0.15% |
0.12% |
STPP |
0.22-O.30% |
0.30% |
H 2 O |
33% |
33% |
PROCESS REQUIREMENT: GLAZE SLIP, SCREENED THROUGH 120MESH, IS APPLIED BY WAY OF A SCRAPER OR A BELL.
REMAINS: 5-7g/100cc(325MESH)
DENSITY: 1.82-1.84
FLOW: 50-60SECONDS
JM-1501
SINGLE FAST FIRING WALL TILE MATT GLAZE(FRIT)
INGREDIENT: SiO 2 -ZrO 2 -TiO 2 -Al 2 O 3 -B 2 O 3 -K 2 O-CaO-MgO-ZnO
EXPANSIVE COEFFICIENT: 190(X10 -7 / ℃ )
INTENERATE TEMPERATURE: 750 ℃
CHARACTERISTICS: FINE SMOOTHNESS AND COMFORTABLE WHITENESS, FINE-COLOR AND WITH A BROAD RANGE OF FIRING, ALKALI-RESISTING AND ACID-RESISTING AND FIRE-RESISTING,
CONDITION FOR USE: 1) SUITABLE FOR SINGLE FAST FIRING WALL TILE.
FIRING ENVIRONMENTAL TEMPERATURE: 1000℃--1040℃(27# TEMPERATURE RING), 1120℃--1150℃ GAUGE READINGS.
2) CAN BE MIXED WITH OPAL GLAZE TO CHANG ITS FIRING TEMPERATURE TO SUIT YOUR REQUIREMENT.
3) CAN BE APPLIED TO ROTOCOLOR LARGE SIZE MATTE GLAZE TILE WITH 1.5-2 TIMES MORE GLAZE APPLICATION THAN AVERAGE.
RECOMMENDED RATIO: GENERAL
MATERIALS
USED |
RATIO RANGE
(GENERAL) |
RATIO
(SPECIFIC) |
JM-1501 |
81-95% |
81% |
JZ-1618 |
0-10% |
10% |
ZnO |
0-5% |
3% |
KAOLIN |
4-6% |
6% |
CMC |
0.12-0.15% |
0.12% |
STPP |
0.22-O.30% |
0.30% |
H 2 O |
30-35% |
33% |
RECOMMENDED RATIO: ROTOCOLOR LARGE-SIZE
MATERIALS
USED |
RATIO RANGE
(GENERAL) |
RATIO
(SPECIFIC) |
JM-1501 |
81-95% |
81% |
JZ-1802 |
0-10% |
10% |
ZnO |
0-5% |
3% |
KAOLIN |
4-6% |
6% |
CMC |
0.12-0.15% |
0.12% |
STPP |
0.22-O.30% |
0.30% |
H 2 O |
30-35% |
33% |
PROCESS REQUIREMENT: GLAZE SLIP, SCREENED THROUGH 120MESH, IS APPLIED BY WAY OF A SCRAPER OR A BELL.
REMAINS: 0.5-1.0g/100cc(325MESH)
DENSITY: 1.86-1.89
FLOW: 50-60SECONDS
JM-2101
DOUBLE FAST FIRING WALL TILE TRANSPARENT( CRYSTAL)FRIT
INGREDIENT: SiO 2 -Al 2 O 3 -K 2 O-Na 2 O - CaO-MgO-B 2 O 3 -ZnO-BaO
EXPANSIVE COEFFICIENT: 185(X10 -7 / ℃ )
INTENERATE TEMPERATURE: 760 ℃
CHARACTERISTICS: FINE SMOOTHNESS AND BRIGHT, TRANSPARENT AND COMFORTABLE WHITENESS, WITH A.BROAD RANGE OF FIRING.
CONDITION FOR USE: SUITABLE FOR DOUBLE FAST FIRING WALL TILE.
FIRING ENVIRONMENTAL TEMPERATURE: 1000℃--1020℃(27# TEMPERATURE RING), 1060℃--1090℃ GAUGE READINGS.
RECOMMENDED RATIO: GENERAL
MATERIALS
USED |
RATIO RANGE
(GENERAL) |
RATIO
(SPECIFIC) |
JT-1808 |
85-90% |
88% |
KAOLIN |
12-15% |
12% |
CMC |
0.12-0.15% |
0.12% |
STPP |
0.22-O.30% |
0.30% |
H 2 O |
33% |
33% |
RECOMMENDED RATIO: COMBINED WITH CRYSTAL FRIT
MATERIALS
USED |
RATIO RANGE
(GENERAL) |
RATIO
(SPECIFIC) |
JT-1819 |
60-90% |
66% |
JZ-1618 |
10-40% |
34% |
KAOLIN |
8-12% |
8% |
CMC |
0.12-0.15% |
0.10% |
STPP |
0.22-O.30% |
0.30% |
H 2 O |
30-35% |
33% |